Polyester Conveyor Belt

Basic product description
Polyester conveyor belts (EP conveyor belts) are widely used in coal, mining, ports, metallurgy, electricity, chemical industry and other fields to transport materials.

PRODUCT DETAILS

Basic product description

Polyester conveyor belts (EP conveyor belts) are widely used in coal, mining, ports, metallurgy, electricity, chemical industry and other fields to transport materials.

Features:

High strength, thin belt body and light weight.

Use EP dipped canvas as the skeleton material.

The belt body is soft, has good troughing and good elasticity.

Impact resistance, wear resistance and corrosion resistance.

Suitable for large load, fast speed and medium and long distance material transportation.

Smooth operation without deviation.

Specifications and technical parameters of polyester multi-layer conveyor belts
Fabric Type Fabric construction Fabric Model Tape thickness Strength Series（N/mm） Covering glue thickness（mm） Width range（mm）
through latitude 2nd floor 3 levels 4th floor Upper cover glue Lower cover glue
Polyester（EP） Polyester Cotton EP-80 1.00 160 240 320 0-12 0-10 300-2500
EP-100 1.00 200 300 400
EP-125 1.05 250 375 500
EP-150 1.10 300 450 600
EP-170 1.10 340 510 680
EP-200 1.20 400 600 800
EP-250 1.40 500 750 1000
EP-300 1.60 600 900 1200
EP-350 1.70 1050 1400
EP-400 1.90 1600
EP-500 2.10 2000

Adhesion strength and elongation performance meet the following table

Adhesive strength, elongation performance
Core material Adhesion strength Extension performance
Between fabric layers
N/mm		 Between cover layer and fabric layerN/mm Full thickness longitudinal
Elongation at break		 Full thickness longitudinal
Reference force elongation
Cover thickness≤1.5mm Cover thickness≥1.5mm
Polyester canvas ≥5 ≥4.5 ≥5 ≥10% ≤4%

The covering performance of the tape complies with the following table

Tape Cover Properties
Covering level Tensile Strength Elongation at break Wear Change rate of tensile strength and elongation at break after aging
Mpa Kgf/cm² % mm³ %
H 24 240 450 120 -25 ~ +25
D 18 180 400 100 -25 ~ +25
L 15 150 350 200 -25 ~ +25